A rapid drying, non-convertible coating for application to ferrous and non-ferrous, decorative and structural metalwork where a high level of corrosion resistance is required. It may also
be used as a primer/finish for most adequately prepared substrates, exhibiting good adhesion
to well-prepared galvanised steel surfaces.
Quick drying by solvent evaporation gives tack free time of 20 minutes.
Ideally suited to airless spray application
Non-sag properties allow good film build to 125 microns d.f.t..
Can be used as a one-coat finish directly to most bare metals. For exterior
exposure, a minimum dry film thickness of 75 microns is recommended. For marine
and coastal environments 125 microns dry film thickness is recommended.
Can be applied down to 5oC.
Tough, flexible film, resistant to many aqueous chemicals.
Surfaces must be dry, sound and free from dirt, dust, rust and grease. Steel surfaces
should be preferably blast cleaned to ISO 8501 part A1 Sa 2½ or wire brushed to BS7079
Part A1 ST2.
Galvanised steel should be free of White rust (zinc corrosion deposits) and if previously
weathered should be washed with copious quantities of water to remove soluble salts.
Galvanised steel that has been oiled should be thoroughly cleaned to remove all traces of
oil prior to coating. Heavily chromated galvanised steel should be alkali cleaned to
remove the chromate passivation. Bright spangled galvanised steel will require abrading
thoroughly using P600 wet or dry abrasive paper ((or similar) prior to degreasing, and
painting.
A low satin finish, stocked in Black and White in 5 litre containers.
An extensive range of
colours are available to order from the MANORMIX scheme.
Touch dry 20-45 mins
overcoat in 1-2 hours